| Ni | Cr | Cu | Sn | Si | Mn |
| 70% | 12% | 12% | 4.5% | 1.0% | 0.5% |
| Density | 8.0g/cm3 deviation is not more than ±5% |
| Solidine temperature | 1250ºC deviation is not.more than ±50ºC |
| Liquidus temperature | 1300ºC deviation is not more than ±50ºC |
| Vickers hardness | 250HV5 deviation is not more than ±10% |
| Linear. expansion coeffcient | 13.8*10-6k-1 deviation is not more than0.5*10-6k-1 |
| Separation/fracture initiation strength | should be greater than 25Mpa |
| 0.2% non-proportional extension strength | ≥270 |
| Elongation at break | ≥5 |