| Customization: | Available |
|---|---|
| Usage: | Polishing Material, Embedded Material, Denture Processing |
| Usage Times: | Disposable |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Co | Cr | Mo | Sr | Si | Mn |
| 61% | 30% | 5.0% | 1.5% | 1.0% | 1.0% |
| Density | 8.0g/cm3 deviation is not more than ±5% |
| Solidine temperature | 1310ºC deviation is not.more than ±50ºC |
| Liquidus temperature | 1370ºC deviation is not more than ±50ºC |
| Vickers hardness | 250HV5 deviation is not more than ±10% |
| Linear. expansion coeffcient | 13.8*10-6k-1 deviation is not more than0.5*10-6k-1 |
| Separation/fracture initiation strength | should be greater than 25Mpa |
| 0.2% non-proportional extension strength | ≥360 |
| Elongation at break | ≥2 |